Alkaline battery

ABSTRACT

An alkaline battery has a positive electrode mixture containing manganese dioxide and a conductive material filling a tubular positive electrode can that is closed at one end. A negative electrode mixture containing a zinc powder filling on an inner peripheral side of a separator is disposed on an inside of the positive electrode mixture. The negative electrode mixture contains zinc particles with a granularity of 75 μm or less at 25 to 40 mass %. The positive electrode mixture has a plurality of tubular pellets stacked inside the positive electrode can coaxially with the positive electrode can. A sum s of lengths of gaps between the pellets is set at 1 to 14% with respect to a sum d of lengths of the pellets. Thus, a sufficient amount of the electrolyte is held in the gaps and between the pellets in the positive electrode.

TECHNICAL FIELD

The present disclosure relates to discharge performance of an alkaline battery and especially relates to improvement in heavy load discharge performance.

BACKGROUND ART

Recently, electronic devices such as digital cameras, video cameras, mobile phones, and smart phones have been improved their performance and downsizing, and requests for improvement in performance of alkaline batteries, which are used as power supplies for such electronic devices, have been increased. Especially, requests for improvement in heavy load discharge performance (high load discharge characteristics) have been increased.

For example, Patent Literature 1 describes a technique to improve the high load discharge characteristics of an alkaline battery as follows. The alkaline battery includes a negative electrode that contains a zinc alloy powder containing fine powders having a grain diameter of 75 μm or less at 20 to 50 weight %, a positive electrode, a separator arranged between the negative electrode and the positive electrode, and an electrolyte. The alkaline battery is configured such that a time period for an electric potential of the negative electrode to rise becomes shorter than a time period for an electric potential of the positive electrode to fall, in constant resistance discharge.

CITATION LIST Patent Literature

Patent Literature 1: Japanese Patent No. 5172181

SUMMARY OF INVENTION Technical Problem

In the above-described Patent Literature 1, the zinc alloy powder containing fine powders having a grain diameter of 75 μm or less at 20 to 50 weight % is used as a negative electrode material to improve heavy load discharge characteristics. However, even when the fine powders are used for the negative electrode material, the heavy load discharge characteristics may not be improved. A reason why this occurs is considered as follow. Such a fine powder of a small grain diameter has a large specific surface, and thus the electrolyte is likely to be held on the negative electrode side. This reduces the electrolyte on the positive electrode side and increases electrical resistance on the positive electrode side.

An aspect of the present disclosure is to improve discharge performance of an alkaline battery, and especially to provide the alkaline battery excellent in heavy load discharge performance.

Solution to Problem

One of the present disclosure to achieve such an aspect is an alkaline battery comprising: a positive electrode mixture filling a tubular positive electrode can closed at one end; a separator disposed on an inner peripheral side of the positive electrode mixture; a negative electrode mixture filling an inner peripheral side of the separator, the negative electrode mixture containing a powder mainly containing zinc; a negative electrode current collector inserted into the negative electrode mixture; a negative electrode terminal plate to seal an opening of the positive electrode can; and an alkaline electrolyte, the positive electrode mixture containing manganese dioxide and a conductive material, the powder containing particles with a granularity of 75 μm or less in a range of 25 to 40 mass %, the positive electrode mixture constituted of a plurality of tubular pellets, the plurality of tubular pellets loaded inside the positive electrode can in such a manner as to be stacked coaxially with the positive electrode can, one or more gaps disposed between the pellets, the gaps and the pellets having a ratio of a sum s of length of the gaps axially along the positive electrode can to a sum d of lengths of the pellets axially along the positive electrode can, the ratio being 1 to 14%.

Another one of the present disclosure according to the above-described alkaline battery is configured as follows. The pellets have a density in a range of 3.0 to 3.7 g/cm³.

Another one of the present disclosure according to the above-described alkaline battery is configured as follows. The pellets contain graphite as the conductive material in a range of 5 to 20 mass % with respect to the manganese dioxide.

Aspects disclosed in the present application and solution thereof will be apparent from Description of Embodiments and the drawings.

Advantageous Effects

The present disclosure can provide an alkaline battery excellent in discharge performance, especially, heavy load discharge performance.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 is a diagram illustrating a configuration of a common cylindrical alkaline battery.

DESCRIPTION OF EMBODIMENTS

FIG. 1 illustrates a configuration of a common cylindrical alkaline battery (LR6 (AA size) alkaline battery), to which the present disclosure is applied (hereinafter referred to as an alkaline battery 1). FIG. 1 is a vertical cross-sectional view illustrating the alkaline battery 1 (cross-sectional view of the alkaline battery 1 when an extension direction of a cylinder axis is set as an up-down (vertical) direction).

As illustrated in FIG. 1, the alkaline battery 1 includes: a tubular metallic battery can closed at one end (hereinafter referred to as a positive electrode can 11); a positive electrode mixture 21 inserted into the positive electrode can 11; a cylindrical separator 22 closed at one end disposed on an inner peripheral side of the positive electrode mixture 21; a negative electrode mixture 23 filling on an inner peripheral side with respect to the separator 22; a negative electrode terminal plate 32 fitted into an opening of the positive electrode can 11 via a sealing gasket 35 made of resin; and a rod-shaped negative electrode current collector 31 made of a material such as a brass. The negative electrode current collector 31 is fixedly installed inside the negative electrode terminal plate 32 by a spot welding or a similar method. The positive electrode mixture 21, the separator 22, and the negative electrode mixture 23 constitute a power generating element 20 of the alkaline battery 1.

The positive electrode can 11 has a conductive property, and is formed, for example, by performing presswork onto a metal material such as a nickel plated steel plate. The positive electrode can 11 doubles as a positive electrode current collector and a positive electrode terminal. A protruding positive electrode terminal portion 12 is formed integrally with a bottom portion of the positive electrode can 11.

The positive electrode mixture 21 is formed as follows. Electrolytic manganese dioxide (EMD) as a positive electrode active material, graphite as a conductive material, and an electrolyte mainly containing a potassium hydroxide (KOH) are mixed together with a binder such as polyacrylic acid. Such a mixture is processed through steps of rolling, disintegration, granulation, classification, and the like, and thereafter is compressed and shaped into rings. As illustrated in FIG. 1, the positive electrode can 11 have the positive electrode mixture 21 that is configured with a plurality of (three) pellets 21 a, 21 b, and 21 c of a tubular shape press-fitted into the positive electrode can 11 in such a manner as to be stacked in a vertical direction, with their cylinder axes being coaxial with the cylinder axis of the positive electrode can 11. The pellets 21 a, 21 b, and 21 c axially along the positive electrode can 11 have respective lengths of d1, d2, and d3 in this order. Although the respective lengths of the pellets 21 a, 21 b, and 21 c coincide with one another (d1=d2=d2) in this embodiment, these lengths may not coincide.

As illustrated in FIG. 1, a gap 51 is disposed between the pellet 21 a and the pellet 21 b and a gap 52 is disposed between the pellet 21 b and the pellet 21 c. The gap 51, which is disposed between the pellet 21 a and the pellet 21 b, has a length of s1 axially along the positive electrode can 11. The gap 52, which is disposed between the pellet 21 b and the pellet 21 c, has a length of s2 axially along the positive electrode can 11. A surface, of the pellet 21 c, on the positive electrode terminal portion 12 side closely contacts the positive electrode can 11.

The negative electrode mixture 23 is produced by gelatinizing a zinc alloy powder as a negative electrode active material. The zinc alloy powder is produced by a gas atomization method or a centrifugal spray method. The zinc alloy powder contains: zinc; an alloy component (e.g., bismuth, aluminum, and indium) added to reduce gas (to prevent liquid leakage); and potassium hydroxide as the electrolyte. The negative electrode current collector 31 is penetrated into the center of the negative electrode mixture 23.

In order to verify the effects of improvement in discharge performance, especially heavy load discharge performance, of the alkaline battery 1 configured as described above, the following Tests 1 to 3 were conducted.

<Test 1>

In Test 1, in order to verify appropriate ranges of granularity of the zinc alloy powder in the negative electrode mixture 23 as well as the gaps 51 and 52 between the pellets constituting the positive electrode mixture 21, the granularity of the zinc alloy powder of the negative electrode mixture 23 was varied (the content percentage of the particles with a granularity of 75 μm or less (hereinafter also referred to as a “proportion of particles with 75 μm or less”) was varied in a range of 20.0 to 45.0 mass %), and also the sizes of the gaps 51 and 52 were varied (the ratio of the sum of lengths of the gaps 51 and 52 axially along the positive electrode can 11, i.e., s=s1+s2, to the sum of lengths of the pellets axially along the positive electrode can 11, i.e., d=d1+d2+d3, (hereinafter also referred to as “gap/mixture height”) was varied). Thus, the plurality of alkaline batteries 1 was manufactured to compare their discharge performance. All alkaline batteries 1 employed the positive electrode mixture 21 having a density (hereinafter also referred to as a “positive electrode mixture density”) of 3.2 g/cm³ and having a ratio of graphite to manganese dioxide in the positive electrode mixture 21 (hereinafter also referred to as a “graphite/manganese dioxide”) of 10.0 mass %.

The discharge performance was compared as follows. A cycle discharge test assuming heavy load discharge, for example, during the use of a digital camera (a cycle of discharge for two seconds at 1500 mW and discharge for 28 seconds at 650 mW was performed ten times for one hour (an idle period for one hour was about 55 minutes)) was conducted. Then, the number of cycles until reaching a cutoff voltage (1.05 V) was counted for comparison.

Table 1 shows results of the discharge performance comparisons among the alkaline batteries 1. The values indicating the discharge performance in Table 1 are relative values, assuming the discharge performance of the alkaline battery 1 in Comparative Example 3 as 100.

TABLE 1 Positive electrode Proportion of particles with Clearance/mixture mixture Graphite/manganese Discharge 75 μm or less (Mass %) height (%) density (g/cm3) dioxide (Mass %) performance Working Example 1 25.0 5.0 3.2 10.0 118 Working Example 2 30.0 5.0 3.2 10.0 125 Working Example 3 40.0 5.0 3.2 10.0 120 Comparative Example 1 20.0 5.0 3.2 10.0 95 Comparative Example 2 45.0 5.0 3.2 10.0 100 Working Example 4 30.0 1.0 3.2 10.0 120 Working Example 5 30.0 8.0 3.2 10.0 127 Working Example 6 30.0 12.0 3.2 10.0 120 Working Example 7 30.0 14.0 3.2 10.0 110 Comparative Example 3 30.0 0.0 3.2 10.0 100 Comparative Example 4 30.0 0.5 3.2 10.0 105 Comparative Example 5 30.0 15.0 3.2 10.0 95

As shown in Table 1, it has been confirmed that the alkaline batteries 1 which contain the particles with a granularity of 75 μm or less, as the zinc alloy powder of the negative electrode mixture 23, in a range of 25 to 40 mass % and which have a ratio of the sum s of the gaps 51 and 52 to the sum d of the axial lengths of the pellets (gap/mixture height) of 1 to 14%, exhibit the high discharge performance (Working Examples 1 to 7). It has been also confirmed that the alkaline batteries 1 containing the particles with a granularity of 75 μm or less, as the zinc alloy powder of the negative electrode mixture 23, in a range of 30 mass % and having a ratio of the sum s of the gaps 51 and 52 to the sum d of the axial lengths of the pellets (gap/mixture height) of 8.0% exhibit outstandingly high discharge performance (Working Example 5).

It has been found from Comparative Example 2 that the excessively large amount of fine powders of the negative electrode mixture 23 does not improve discharge performance. It is considered that this is because the electrolyte was likely to be held on the negative electrode side due to the fine powders having a small grain diameter and a large specific surface, and this reduced the electrolyte on the positive electrode side, resulting in an increase in electrical resistance on the positive electrode side.

Further, it has been found from Comparative Examples 3 and 4 that the excessively small gaps 51 and 52 do not improve discharge performance. It is considered that this is because the sufficient amount of electrolyte results in not being held on the positive electrode side due to the excessively small gaps 51 and 52.

Furthermore, it has been found from Comparative Example 5 that the excessively large gaps 51 and 52 do not improve discharge performance. It is considered that this is because the excessively large gaps 51 and 52 reduce the amount of negative electrode active material oppose to the positive electrode active material, resulting in an increase in current density.

<Test 2>

Subsequently, in order to verify an appropriate range of the density of the positive electrode mixture 21 (positive electrode mixture density), the plurality of alkaline batteries 1 including the positive electrode mixtures 21 with their densities varied (the densities of the positive electrode mixtures 21 were varied in a range of 2.8 to 3.7 g/cm³) were manufactured to compare their discharge performance. It should be noted that all the alkaline batteries 1 had a ratio of the sum s of the gaps 51 and 52 to the sum d of the axial lengths of the pellets (gap/mixture height) of 5.0%. Further, all the alkaline batteries 1 employed the positive electrode mixture 21 having a ratio of graphite to manganese dioxide in the positive electrode mixture 21 (graphite/manganese dioxide) of 10.0 mass %. The discharge performance was obtained by a method similar to Test 1.

Table 2 shows the results of the discharge performance comparisons among the alkaline batteries 1. It should be noted that the values indicating the discharge performance in Table 2 are relative values, assuming the discharge performance of the alkaline battery 1 in Comparative Example 3 shown in Table 1 as 100.

TABLE 2 Clearance/ Positive electrode Proportion of particles with mixture mixture Graphite/manganese Discharge 75 μm or less (Mass %) height (%) density (g/cm3) dioxide (Mass %) performance Working Example 8 30.0 5.0 3.0 10.0 128 Working Example 9 30.0 5.0 3.7 10.0 123 Comparative 30.0 5.0 3.9 10.0 Mixture cannot be manufactured. Example 6 Comparative 30.0 5.0 2.8 10.0  86 Example 7

As shown in Table 2, it has been confirmed that the discharge performance of the alkaline batteries 1 is enhanced with the density of the positive electrode mixture 21 (positive electrode mixture density) in a range of 3.0 to 3.7 g/cm³ (Working Examples 8 and 9). It has been also confirmed that the discharge performance is outstandingly enhanced with the density of the positive electrode mixture 21 of 3.0 g/cm³ (Working Example 8).

The excessively high density of the positive electrode mixture 21 was likely to cause cracking, resulting in difficulty in compression molding, thereby failing to manufacture the pellets (Comparative Example 6).

The excessively low density of the positive electrode mixture 21 failed to obtain the sufficient discharge performance (Comparative Example 7). It is considered that this is because the excessively low density of the positive electrode mixture 21 causes insufficient conductivity inside the positive electrode mixture 21.

<Test 3>

Subsequently, in order to verify an appropriate range of the ratio of graphite to manganese dioxide in the positive electrode mixture 21 (graphite/manganese dioxide), the plurality of alkaline batteries 1 with their ratios varied (the ratios were varied in a range of 2.0 to 25.0 mass %) were manufactured to compare their discharge performance. The discharge performance was obtained by the method similar to the above-described method. All the alkaline batteries 1 had a ratio of the sum s of the gaps 51 and 52 to the sum d of the axial lengths of the pellets (gap/mixture height) of 5.0%. Further, all the alkaline batteries 1 employed the density of the positive electrode mixture 21 (positive electrode mixture density) of 3.2 g/cm³.

Table 3 shows the results of the discharge performance comparisons among the respective alkaline batteries 1. It should be noted that the values indicating the discharge performance in Table 3 are relative values, assuming the discharge performance of the alkaline battery 1 in Comparative Example 3 shown in Table 1 as 100.

TABLE 3 Clearance/ Positive electrode Proportion of particles with mixture mixture Graphite/manganese Discharge 75 μm or less (Mass %) height (%) density (g/cm3) dioxide (Mass %) performance Working Example 10 30.0 5.0 3.2 5.0 126 Working Example 11 30.0 5.0 3.2 15.0 132 Working Example 12 30.0 5.0 3.2 20.0 119 Comparative Example 8 30.0 5.0 3.2 2.0 77 Comparative Example 9 30.0 5.0 3.2 25.0 85

As shown in Table 3, it has been confirmed that the discharge performance is enhanced with the ratio of graphite to manganese dioxide in the positive electrode mixture 21 (graphite/manganese dioxide) in a range of 5 to 20 mass % (Working Examples 10 to 12). It has been also confirmed that the discharge performance is outstandingly enhanced with the ratio of graphite to manganese dioxide in the positive electrode mixture 21 (graphite/manganese dioxide) of 15.0 mass % (Working Example 11).

The excessively small ratio of the graphite failed to obtain sufficient discharge performance (Comparative Example 8). It is considered that this is caused by insufficient conductivity inside the positive electrode mixture 21.

The excessively large ratio of the graphite failed to obtain sufficient discharge performance (Comparative Example 9). It is considered that this is because the amount of electrolyte was reduced in the positive electrode mixture 21 due to an influence from the water-repellent graphite.

<Effects>

As described above, the following has been found. The discharge performance of the alkaline battery 1 is enhanced in the case where the negative electrode mixture 23 contains, as the zinc alloy powder, particles with a granularity of 75 μm or less in a range of 25 to 40 mass % and the ratio of the sum s of the gaps 51 and 52 to the sum d of the axial lengths of the pellets are set to 1 to 14%. The satisfactory results are obtained especially in the case where the negative electrode mixture 23 containing, as the zinc alloy powder, particles with a granularity of 75 μm or less in the range of 30 mass % is employed and the ratio of the sum s to the gaps 51 and 52 to the sum d of the axial lengths of the pellets is set to 8.0%.

It has been confirmed that the discharge performance is enhanced in the case where the positive electrode mixture 21 has a density in a range of 3.0 to 3.7 g/cm³. It has been found that the satisfactory results are obtained especially in the case where the positive electrode mixture 21 has a density of 3.0 g/cm³.

It has been confirmed that the discharge performance is enhanced in the case where the ratio of graphite to manganese dioxide in the positive electrode mixture 21 (graphite/manganese dioxide) is in a range of 5 to 20 mass %. It has been found that the satisfactory results are obtained especially in the case where the ratio of graphite to manganese dioxide in the positive electrode mixture 21 (graphite/manganese dioxide) is 15.0 mass %.

The description of the above-described embodiment is for ease of understanding of the present disclosure and does not limit the present disclosure. The present disclosure may be modified or improved without departing from the gist and includes the equivalents.

For example, the above-described embodiment configures the number of pellets constituting the positive electrode mixture 21 to be three. However, the number of pellets may be two or four or more. In short, it is only necessary that the ratio of the sum s of the lengths of the gap(s) between the pellets axially along the positive electrode can 11 to the sum d of the lengths of the pellets axially along the positive electrode can 11 meets the above-described conditions, together with other necessary conditions. This ensures the above-described effects.

REFERENCE SIGNS LIST

-   1 alkaline battery -   11 positive electrode can -   12 positive electrode terminal portion -   20 power generating element -   21 positive electrode mixture -   21 a, 21 b, 21 c pellet -   22 separator -   23 negative electrode mixture -   31 negative electrode current collector -   32 negative electrode terminal plate -   35 sealing gasket -   51, 52 gap 

1. An alkaline battery comprising: a positive electrode mixture filling a tubular positive electrode can closed at one end; a separator disposed on an inner peripheral side of the positive electrode mixture; a negative electrode mixture filling an inner peripheral side of the separator, the negative electrode mixture containing a powder mainly containing zinc; a negative electrode current collector inserted into the negative electrode mixture; a negative electrode terminal plate to seal an opening of the positive electrode can; and an alkaline electrolyte, the positive electrode mixture containing manganese dioxide and a conductive material, the powder containing particles with a granularity of 75 μm or less in a range of 25 to 40 mass %, the positive electrode mixture constituted of a plurality of tubular pellets, the plurality of tubular pellets stacked and loaded inside the positive electrode can in such a manner as to be stacked coaxially with the positive electrode can, a gap disposed between the pellets, the gaps and the pellets having a ratio of a sum s of length of the gaps axially along the positive electrode can to a sum d of lengths of the pellets axially along the positive electrode can, the ratio being 1 to 14%.
 2. The alkaline battery according to claim 1, wherein the pellets have a density in a range of 3.0 to 3.7 g/cm³,
 3. The alkaline battery according to claim 1, wherein the pellets contain graphite as the conductive material in a range of 5 to 20 mass % with respect to the manganese dioxide. 